XP 100 (ER 100S-G) WIRE (0.8MM) 15KG
Login to see prices
SKU: XP15254High Strength MIG Wire
- Low-alloyed solid wire designed for welding fine-grained, quenched and tempered high-strength steels.
- Provides a minimum yield strength of 550 MPa.
- Offers superior crack resistance and weld integrity.
- Excellent mechanical properties at subfreezing temperatures down to -50°C.
- Widely used in the construction of high-strength pipelines, earthmoving and mining equipment, trucks, mobile cranes, concrete pumps and lifting equipment.
Welding Positions:
Additional Information
| Material | Low Alloy |
|---|---|
| Base Materials | T1, T1A, T1B, StE460, StE590, X60, X65, X70, X80, S460, S500, S550, S620, Weldox |
| Temperature | '-50ºC |
| Size | 0.8mm, 1.0mm, 1.2mm, 1.6mm |
| Weight | 15kg |
| Spool | BS300 |
| Shielding Gas | Mixed Gas |
| Current Type | DC+ |
| Elongation | 20% (≥18%) |
| Tensile Strength MPa | 730 (640 - 820) |
| Yield Strength | 640 (≥550) |
| 0.2% Proof Stress Rp 0.2 | ?620MPa (C1/SG-C Shielding Gas), '?690MPa (M21/SG-AC-25 Shielding Gas) |
| Impact Energy iso-V | 50J (≥47J) |
| Chemical Composition (%) | Al = 0.12, C = 0.14, Cr = 0.40 MIN - 0.65 MAX, Cu = 0.30, Mn = 1.30 MIN - 1.80 MAX, Mo = 0.15 MIN - 0.30 MAX, Ni = 0.50 MIN - 0.65 MAX, P = 0.015, S = 0.018, Si = 0.60 MIN - 0.80 MAX, Ti = 0.10, V = |
| Grade | ER100S-G, AWS A5.28, G 55 5 M21 Mn3NiCrMo |
| Conforms To | A5.28: ER100S-G, EN ISO 16834-A |
| Set Size | Single Box |