XP A18 (ER 70S-6) TIG WIRE (1.0MM) 5KG

SKU: XP10324

Mild Steel TIG Wire

Double-deoxidized wire for welding mild and low alloy steels require a minimum 420 MPa yield strength.
High silicon content promotes weld pool fluidity, offering a smoother bead appearance and minimal post-weld grinding.
Particularly well-suited for root and final capping passes when joining pipes.
Excellent mechanical properties at subfreezing temperatures down to -40°C.
Widespread usage across a diverse range of industries and applications, such as boiler manufacturing, heavy industrial machinery, shipbuilding, chemical plants, petroleum refineries, water supply lines, natural gas pipeline, automotive manufacturing, railroad equipment, structural steel fabrication and various engineering projects.

Welding Positions:
"Welding

Material	Mild Steel
Base Materials	S235JR-S355JR, S235J0-S355J0, S235J2-S355J2, S275N-S420N, S275M-S420M, P235GH-P355GH, P275NL1-P355NL1, P215NL, P265NL, P355N, P285NH-P420NH, P195TR1-P265TR1, P195TR2-P265TR2, P195GH-P265GH, L245NB-L4
Temperature	'-40ºC
Size	1.0mm, 1.2mm, 1.6mm, 2.4mm, 3.2mm
Weight	5kg
Shielding Gas	Pure Argon
Current Type	DC+
Chemical Composition (%)	Al = 0.02, C = 0.06 MIN - 0.14 MAX, Cr = 0.15, Mn = 1.30 MIN - 1.60 MAX, Mo = 0.15 MAX, Ni = 0.15, P = 0.025, S = 0.025, Si = 0.70 MIN - 1.00 MAX, Ti + Zr = 0.15, V = 0.03
Elongation	24% (≥20%)
Tensile Strength MPa	24 (≥20)
Yield Strength MPa	450 (≥420)
0.2% Proof Stress Rp 0.2	?400MPa
Impact Energy iso-V	80J (≥47J)
Grade	ER70S-6
Conforms To	AWS A5.18 ER70S-6, EN ISO 636-A: W 42 4 3Si1
Set Size	Single Box
Packaging Type	PAP 20 Tube